TECHNICAL INFORMATION

 Home / CARBON STEEL PIPE

CARBON STEEL PIPE

CHEMICAL ANALYSIS
 Mechnical Properties SPECIFIC REQUIREMENT
Tensile Strength Yield Strength Elongation
Specification WT C% Mn% P% MAX S% MAX Si% Cr% Mo% Mpa Mpa 50mm MIN Longitudinal  
ASTM A 53/A AW 0.25MAX 0.95MAX 0.050 0.060 - - - 331MIN 207 MIN 36 Cr     Mo   Cu 
ASTM A 53/B AW 0.30MAX 1.20MAX 0.050 0.060 - - - 413MIN 240MIN 29.5 Ni    Va
ASTM A 106/A AW 0.25MAX 0.27-0.93 0.025 0.025 0.10MIN 0.40MAX 0.15MAX 330MIN 205MIN 35/28 0.40 0.15 0.40 0.40
ASTM A 106/B AW 0.30MAX 0.29-1.06 0.025 0.025 0.10MIN 0.40MAX 0.15MAX 415MIN 240MIN 30/22 0.08
ASTM A 106/C AW 0.35MAX 0.29-1.06 0.025 0.025 0.10MIN 0.40MAX 0.15MAX 485MIN 275MIN 30/22 five elements not to exceed 1%
ASTM A 179 MW 0.06-018 0.27-0.63 0.048 0.048 - - - 325MIN 180MIN 35.0 Hardness 72 HRB MAX
ASTM A 214 MW 0.18MAX 0.27-0.63 0.050 0.050 - - - 385MIN 180MIN 35.0 Hardness 72 HRB MAX
ASTM A 192 MW 0.06-0.18 0.27-0.63 0.048 0.048 0.25MAX - - 325MIN 180MIN 35.0 Hardness 77 HRB MAX
ASTM A 209/T1 MW 0.10-0.20 0.30-0.80 0.045 0.045 0.10-0.50 - 0.44-0.65 380MIN 205MIN 30/22 Hardness 80 HRB MAX
ASTM A 209/T1a MW 0.15-0.25 0.30-0.80 0.045 0.045 0.10-0.50 - 0.44-0.65 365MIN 195MIN 30/22 Hardness 81 HRB MAX
ASTM A 209/T1B MW 0.14MAX 0.30-0.80 0.045 0.045 0.10-0.50 - 0.44-0.65 415MIN 220MIN 30/22 Hardness 77 HRB MAX
ASTM A 210/A-1 MW 0.27MAX 0.93MAX 0.048 0.058 0.10MIN - - 415MIN 255MIN 30/22 Hardness 79 HRB MAX
ASTM A 210/C MW 0.35MAX 0.29-1.06 0.048 0.058 0.10MIN - - 485MIN 275MIN 30/22 Hardness 89 HRB MAX
ASTM A 213/T2 MW 0.10/0.20 0.30-0.61 0.045 0.045 0.10-0.30 0.50-0.81 0.44-0.65 415MIN 205MIN 30/22 Hardness 85 HRB MAX
ASTM A 213/T5 MW 0.15MAX 0.30-0.60 0.030 0.030 0.50MAX 4.00-6.00 0.44-0.65 415MIN 205MIN 30/22 Hardness 85 HRB MAX
ASTM A 213/T11 MW 0.15MAX 0.30-0.60 0.030 0.030 0.50-1.00 1.00-1.50 0.44-0.65 415MIN 205MIN 30/22 Hardness 85 HRB MAX
ASTM A 213/T12 MW 0.15MAX 0.30-0.61 0.045 0.045 0.50MAX 0.80-1.25 0.44-0.65 415MIN 205MIN 30/22 Hardness 85 HRB MAX
ASTM A 213/T22 MW 0.15MAX 0.30-0.60 0.030 0.030 0.50MAX 1.90-2.60 0.87-1.13 415MIN 205MIN 30/22 Hardness 85 HRB MAX
ASTM A 333/1 AW 0.30MAX 0.40-1.06 0.025 0.025 - - - 380MIN 205MIN 25/20 Impact AS-50F
ASTM A 333/6 AW 0.30MAX 0.29-1.06 0.025 0.025 0.10MIN - - 415MIN 240MIN 30/22 FOR 40X10J/18/14
ASTM A 334/1 AW 0.30MAX 0.40-1.06 0.025 0.025 - - - 380MIN 205MIN 35/28 -50F 40X10J/18/14
ASTM A 334/6 AW 0.30MAX 0.29-1.06 0.025 0.025 0.10MIN - - 415MIN 240MIN 30/22 90 HRB MAX
ASTM A 335/P1 AW 0.10-0.20 0.30-0.80 0.025 0.025 0.10-0.50 - 0.44-0.65 380MIN 205MIN 30/22  
ASTM A 335/P2 AW 0.10-0.20 0.30-0.61 0.025 0.025 0.10-0.30 0.50-0.81 0.44-0.65 380MIN 205MIN 30/22  
ASTM A 335/P5 AW 0.15MAX 0.30-0.60 0.025 0.025 0.50MAX 4.00-6.00 0.45-0.65 415MIN 205MIN 30/22  
ASTM A 335/P9 AW 0.15MAX 0.30-0.60 0.025 0.025 0.25-1.00 8.00-10.00 0.09-1.10 415MIN 172MIN 30/22  
ASTM A 335/P11 AW 0.15MAX 0.30-0.60 0.025 0.025 0.50-1.00 1.00-1.50 0.44-0.65 415MIN 205MIN 30/22  
ASTM A 335/P12 AW 0.15MAX 0.30-0.61 0.025 0.025 0.50MAX 0.80-1.25 0.44-0.65 415MIN 205MIN 50/22  
ASTM A 335/P22 AW 0.15MAX 0.30-0.60 0.025 0.025 0.50MAX 1.90-2.60 0.87-1.13 415MIN 205MIN 30/22  
BS/3059/1/33 0.15MAX 0.30-0.70 0.050 0.050 - - - 324-441 186MIN 25  
BS/3059/2/33   0.15MAX 0.40-0.70 0.050 0.050 0.10-0.35 - - 324-441 186MIN 21  
BS/3059/2/45   0.12-0.18 0.90-1.20 0.035 0.035 0.10-0.35 - - 441-560 245MIN 22  
BS/3059/2/620   0.10-0.15 0.40-0.70 0.040 0.040 0.10-0.35 0.70-1.10 0.45-0.65 441-618 235MIN 22  
DIN/17175/ST35.8   0.17MAX 0.40MIN 0.040 0.040 0.35MAX - - 340-441 235MIN 25  
DIN/17175/ST45.8   0.22MAX 0.45MIN 0.040 0.040 0.10-0.35 - - 441-540 255MIN 25  
DIN/17175/15MO3   0.12-0.20 0.50-0.80 0.040 0.040 0.10-0.35 - 0.25-0.35 441-540 284MIN 21  
DIN/17175/13CrMO44   0.10-0.18 0.40-0.70 0.040 0.040 0.10-0.35 0.70-1.60 0.40-0.50 441-570 294MIN 22  
DIN/17175/10CrM910   0.15MAX 0.40-0.60 0.040 0.040 0.15-0.50 2.0-2.5 0.9-1.10 441-570 294MIN 22  
ASTM A 199/T5 MW 0.50-0.15 0.30-0.60 0.030 0.030 0.50MAX 4.00-6.00 0.45-0.65 415MIN 170MIN 30/22 Hardness 85 HRB MAX
ASTM A 199/T11 MW 0.50-0.15 0.30-0.60 0.030 0.030 0.50-1.00 1.00-1.50 0.44-0.65 415MIN 170MIN 30/22 Hardness 85 HRB MAX
ASTM A 199/T22 MW 0.50-0.15 0.30-0.60 0.030 0.030 0.50MAX 1.90-2.60 0.87-1.13 415MIN 170MIN 30/22 Hardness 85 HRB MAX
ASTM A 199/T4 MW 0.15MAX 0.30-0.60 0.030 0.030 0.50-1.00 2.15-2.85 0.44-0.65 415MIN 170MIN 30/22 Hardness 85 HRB MAX
ASTM A 199/T7 MW 0.15MAX 0.30-0.60 0.030 0.030 0.50-1.00 6.00-8.00 0.45-0.65 415MIN 170MIN 30/22 Hardness 85 HRB MAX
ASTM A 200/T5 MW 0.15MAX 0.30-0.60 0.030 0.030 0.50-1.00 4.00-6.00 0.45-0.65 415MIN 170MIN 30/22 Hardness 85 HRB MAX
ASTM A 200/T11 MW 0.50-0.15 0.30-0.60 0.030 0.030 0.50-1.00 1.00-1.50 0.44-0.65 415MIN 170MIN 30/22 Hardness 85 HRB MAX
ASTM A 200/T22 MW 0.50-0.15 0.30-0.60 0.030 0.030 0.50MAX 1.90-2.60 0.87-1.13 415MIN 170MIN 30/22 Hardness 85 HRB MAX
ASTM A 200/T4 MW 0.50-0.15 0.30-0.60 0.030 0.030 0.50-1.00 2.15-2.85 0.44-0.65 415MIN 170MIN 30/22 Hardness 85 HRB MAX
ASTM A 200/T7 MW 0.15MAX 0.30-0.60 0.030 0.030 0.50-1.00 6.00-8.00 0.45-0.65 415MIN 170MIN 30/22 Hardness 85 HRB MAX
ASTM A 199/T9 MW 0.15MAX 0.30-0.60 0.030 0.030 0.25-1.00 8.00-10.0 0.90-1.10 415MIN 170MIN 30/22 Hardness 85 HRB MAX

About Us

United Tubes Industries is a leading Stockist & Supplier of all Ferrous & Non-Ferrous Metals.As a pioneer and leader in the Supplier industry, United Tubes Industries is at the forefront of technology and research.

Contact Us

Our Products

Third Party Inspection

Copyright © 2018 United Tubes Industries All rights reserved. Designed By Mesotek